Mn13 High Manganese Wear Resistant Steel Plate
MN13 Resistant steel plate is a kind of high-manganese wear-resistant steel,designed containing around 13% of manganese content.Mn13 High Manganese Wear- Resistant Steel Plates are produced possessing superior hardness and resistance to wear across different environments. The MN13 Manganese Steel Plates showcase good strength and are designed containing good carbon content coupled with the existing manganese content.
The addition of MN in the production process can effectively reduce the cost of equipment wearing parts, save equipment maintenance costs, and improve the competitiveness of finished products. The greater the external impact, the higher the wear resistance of the surface layer of the MN13 Resistant steel plate, which has excellent wear resistance against strong impact wear and high stress wear. As the surface hardened layer gradually wears, the new work hardened layer will continue form. It is an ideal choice among wear-resistant materials such as resistance to strong impacts and high pressure materials.
The versatile MN13 Wear Resistant Steel Plates are resistant to sliding around and show excellent impact resistance due to their enhanced toughness. MN13 Manganese Steel Plate plates provide stability to different components as they are subjected to vigorous stress and torsionacross different setups.
MN13 Manganese Steel Plate Specification
|
Length |
4m-12m or as required |
||
|
Width |
0.6m-3m or as required |
||
|
Thickness |
3mm-300mm or as required |
||
|
Standard |
AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
||
|
Technique |
Hot rolled or cold rolled |
||
|
Surface Treatment |
Clean, blasting and painting according to customer requirement |
||
|
Thickness tolerance |
±0.1mm |
||
|
Material |
Mn13 steel | ||
| Processing services | bending, welding, uncoiling, cutting, punching | ||
|
Application |
It is widely used in small tools, small components, iron wire, siderosphere, pull rod, ferrule, weld assembly, structural metal, |
||
|
Export packing |
Waterproof paper, and steel strip packed.Standard Export Seaworthy Package.Suit for all kinds of transport,or as required |
||
MN13 Manganese Plate Main Feature
-MN13 Resistant steel plate will not be broken during use;
-It has easy machining properties such as easy cutting, welding, bending, etc.;
-Has good welding performance;
-It is easy to be coated and processed, has a variety of varieties, and has a wide range of uses.
Mn13 is the best choice for strong impact resistance, high pressure material wear and other wear-resistant materials, with Work hardening characteristic that other wear-resistant materials can not be compared to, in the larger impact load or the role of greater contact stress, plate surface production hardening, surface hardness from HB200 quickly lifted to more than HB500, This results in a high abrasion resistant surface layer, while the steel plate inner austenite still maintains good impact toughness.
Chemical Composition of Manganese Plate Mn13
| Grade | Mn | C | S | Si | P |
| Mn13 | 11.00 - 14.00 | 0.090 - 1.020 | ≤0.030 | 0.030 - 0.080 | ≤0.035 |
MN13 Steel Hot Rolled Plates Mechanical Strength
| Tensile Properties | Impact property 20°C | Hardness value | Reduction | Value of initial hardness(HB) | |
| Grade | area A(%) | Rm(Mqa) | |||
| Mn13 | ak ≥ 90(J) | > 300 | ≥40% | ≥800MPa | 200 - 250 |
Hot Tags: mn13 high manganese wear resistant steel plate, China mn13 high manganese wear resistant steel plate manufacturers, suppliers, factory, NM300 Wear resistant Steel Plate, NM400 Wear Resistant Steel Plate, NM360 Abrasion Resistant Steel Plate, NM500 Resistant Steel Wear Plate, NM400 Wear Resistant Sheet, NM650 Wear Resistant Steel Plate