310 Stainless Steel Sheet

Alloy 310 (UNS S31000) is an austenitic stainless steel developed for use in high temperature corrosion resistant applications. The alloy resists oxidation up to 2010oF (1100oC) under mildly cyclic conditions.
Surface：No.1, 1D, 2D, 2B, Polished, Brushed, Mirror, Customized
Size：Customized
Material：201, 202, 301, 302, 303, 304, 304L, 304H, 310S, 316, 316L, 317L, 321,310S 309S, 410, 410S,420, 430, 431, 440A,904L
Color：Customized

Send Inquiry

Description

310 Stainless Steel Sheet is a popular high-temperature performance austenitic stainless steel that offers superior resistance to corrosion and oxidation under extreme temperatures.

Type 310 stainless is an austenitic heat resistant alloy with excellent resistance to oxidation under mildly cyclic conditions through 2000 °F. Its high chromium and nickel contents provide comparable corrosion resistance, superior resistance to oxidation and the retention of a larger fraction of room temperature strength than the common austenitic alloys like Type 304. Stainless 310 is often used at cryogenic temperatures, with excellent toughness to -450 °F.

Specification

product-700-522

Product Name	Stainless Steel Sheet
Thickness	Cold rolled:0.1~3.0mm
Thickness	Hot rolled:3mm~500mm
Size	Length:0.1m~12m (All Sizes Can be customzied)
Size	Width:1000mm/1219mm/1240mm/1500mm
Material Grade	201, 202, 301, 302, 303, 304, 304L, 304H, 310S, 316, 316L, 317L, 321,310S 309S, 410, 410S,420, 430, 431, 440A,904L
Standard	ASTM, JIS, GB, AISI, DIN, BS,EN
Package	clients' requirement and Standard export sea-worthy packing

Alloy 310 (UNS S31000) is an austenitic stainless steel developed for use in high temperature corrosion resistant applications. The alloy resists oxidation up to 2010°F (1100°C) under mildly cyclic conditions.

This 310 Stainless Steel Sheet contains approximately 25% chromium, 20% nickel, and a small amount of manganese, which makes it excellent for use in various heat-resistant applications.

310 Stainless Steel Chemical Analysis

Weight % (all values are maximum unless a range is otherwise indicated)

Element	310
Chromium	24.0 min.-26.0 max.
Nickel	19.0 min.-22.0 max.
Carbon	0.25
Manganese	2.00
Phosphorus	0.045
Sulfer	0.030
Silicon	1.50
Iron	Balance

310 Stainless Steel Mechanical Properties[Typical Values at 68°F (20°C)]

Yield Strength 0.2% Offset		Ultimate Tensile Strength		Elongation in 2 in.	Hardness
psi (min.)	(MPa)	psi (min.)	(MPa)	% (min.)	(max.)
35,000	245	80,000	550	45	217 Brinell

310 Stainless Steel Sheet is highly resistant to scaling and corrosion at elevated temperatures, which makes it ideal for use in heat treatment applications such as furnace parts, heat exchangers, and kiln components. Its high nickel content gives it excellent resistance to sulfidation and chloride stress cracking, which makes it even more suitable for harsh environments.

product-700-642