Grade Mn13 is a high-strength, wear-resistant steel, It is made up of a high amount of manganese, which gives it its unparalleled strength and durability,that is commonly used in a variety of industrial applications.
This steel is composed of manganese alloy, which gives it exceptional toughness and durability. Mn13 steel is known for its exceptional ability to withstand abrasive wear, making it an ideal choice for use in mining machinery, construction equipment, and other heavy-duty machinery.
Under the action of large impact load or large contact stress, the surface of the Mn13 steel plate is work hardened, and the surface hardness is rapidly increased from hb200 to above hb500, Thus, a high wear-resistant surface layer is produced, while the austenite in the inner layer of the steel plate still maintains good impact toughness.
MN13 Manganese Steel Plate Details
| Item | MN13 Steel |
|---|---|
| Width | 1000 upto 3000mm |
| Standard Grade | DIN : 1.3401, XAR400, XAR300, XAR450, XAR600, XAR500, X120Mn12 EN : QUARD450, QUARD400, QUARD500; RAEX320, RAEX500, RAEX400 NF : FORA500, FORA400,; Creusabro8000, Creusabro4800 GB : NM360, Mn13, NM600, NM400, NM450, NM500, NM550 JIS : JFE-EH400, JFE-EH360, JFE-EH500; WEL-HARD500, WEL-HARD400 |
| Delivery State | controlled rolling, hot-rolled, normalizing, tempering, annealing, quenching, N+T, Q+T |
| Thickness | 2 upto 300mm |
| Surface | clean, blasting, finishing, and painting |
| Length | 1000 upto 12000mm |
The MN13 Steel Hot Rolled Plate is processed at extreme temperatures in mills where the plates reaches its recrystallization limit and is shaped in correct dimensions. Steel Grade MN13 Plates are difficult to machine and process as the content that makes them wear resistant makes it hard for the plates to be shaped in correct dimensions.
MN13 Grade High Manganese Plates showcase superior tensile and yield strength and provide good support to different components. The robust MN13 Grade Manganese Plate is designed by our renowned workers making use of the best raw materials and cutting edge technology. These plates are further put through vigorous testing to eliminate any flaws in them. For any queries or questions, contact us or visit any of our outlets for more information.
Characteristics of MN13 Grade High Manganese Plates
- Resistance to high abrasion and severe impact.
- Will work hardened rapidly to 550BHN.
- Remains ductile throughout.
- Can be welded.
- Has non-magnetic properties.
- Can be cut with oxy-acetylene torch, plasma, water jet, or laser.
- Made to the toughest standards in the industry for extended service life.
Owes high-performance characteristics to Mn13 unique chemical composition, which includes a high amount of manganese.
MN13 Grade Manganese Plate Packaging and Delivery
Packing details: Pack according to customer requirements.
Port: Qingdao Port, Tianjin Port, etc.
MN13 Grade High Manganese Plates Production Process
About us
As one of the China most trusted and reliable suppliers of Iron&Steel, we have a solution that works for you. Our sheet metal fabrication services are second to none, and we're completely dedicated to your satisfaction.
Contact us if you need specific sizes or grain direction.
Hot Tags: mn13 steel hot rolled high manganese plates, China mn13 steel hot rolled high manganese plates manufacturers, suppliers, factory, NM650 Wear Resistant Steel Plate, NM300 Wear resistant Steel Plate, NM400 Wear Resistant Steel Plate, NM500 Resistant Steel Wear Plate, NM360 Abrasion Resistant Steel Plate, Wear Resistant Steel Plate